NGAC P907-04

High Glass Transition Temperature Fiber Optic Adhesive

To request a FREE sample of NGAC P907-04, complete the form or email us directly at info@nextgenadhesives.com.

See this form in the original post

DESCRIPTION:

NGAC P907-04 is a low viscosity and room temperature curing adhesive specifically formulated for fiber optic terminations.

ADVANTAGES AND APPLICATIONS:

Uses include the termination of single-mode and multi- mode fiber optic connectors, as well as, bonding prisms and lenses. NGAC P907-04 is a low viscosity mixture that ensures exceptional wicking and wetting of the fibers, along with superior adhesion strength to glass and other low surface energy substrates. NGAC P907-04 is blue after cure which will facilitate the polishing process.

NGAC P907-04 with the ability to cure completely at room temperature is used extensively in field termination kits.

NGAC P907-04 features the following characteristics that enable ease of use.

PROPERTIES:

*All values reported below are typical values and are for reference use only. These values are not intended for use in developing specifications. Application testing under specific conditions should be performed to determine actual results and fitness for use.

COLOR (mixed):

Resin - Clear

Hardener - Dark Blue

Mixed - Dark Blue

VISCOSITY (INITIAL): 1,800 cps

SPECIFIC GRAVITY: 1.10

REFRACTIVE INDEX: 1.52

MIX RATIO BY WEIGHT (R/H): 100/30

HARDNESS SHORE D: 83

OPERATING TEMPERATURE: -60 TO +120°C

GLASS TRANSITION (Tg), ULTIMATE: 95°C

PERCENT SOLIDS: 100%

POT LIFE: 30-35 minutes

CURE SCHEDULE:

Temperature of 25˚C for 24 hours

OR

Temperature of 65˚C for 1 hour

OR

Temperature of 90°C for 15 minutes

For additional information or assistance, please call 978-436-9600.