NGAC P907-04
High Glass Transition Temperature Fiber Optic Adhesive
To request a FREE sample of NGAC P907-04, complete the form or email us directly at info@nextgenadhesives.com.
DESCRIPTION:
NGAC P907-04 is a low viscosity and room temperature curing adhesive specifically formulated for fiber optic terminations.
ADVANTAGES AND APPLICATIONS:
Uses include the termination of single-mode and multi- mode fiber optic connectors, as well as, bonding prisms and lenses. NGAC P907-04 is a low viscosity mixture that ensures exceptional wicking and wetting of the fibers, along with superior adhesion strength to glass and other low surface energy substrates. NGAC P907-04 is blue after cure which will facilitate the polishing process.
NGAC P907-04 with the ability to cure completely at room temperature is used extensively in field termination kits.
NGAC P907-04 features the following characteristics that enable ease of use.
PROPERTIES:
*All values reported below are typical values and are for reference use only. These values are not intended for use in developing specifications. Application testing under specific conditions should be performed to determine actual results and fitness for use.
COLOR (mixed):
Resin - Clear
Hardener - Dark Blue
Mixed - Dark Blue
VISCOSITY (INITIAL): 1,800 cps
SPECIFIC GRAVITY: 1.10
REFRACTIVE INDEX: 1.52
MIX RATIO BY WEIGHT (R/H): 100/30
HARDNESS SHORE D: 83
OPERATING TEMPERATURE: -60 TO +120°C
GLASS TRANSITION (Tg), ULTIMATE: 95°C
PERCENT SOLIDS: 100%
POT LIFE: 30-35 minutes
CURE SCHEDULE:
Temperature of 25˚C for 24 hours
OR
Temperature of 65˚C for 1 hour
OR
Temperature of 90°C for 15 minutes
For additional information or assistance, please call 978-436-9600.